ABSTRACT Porous, nano-architected metals with dimensions down to ~10 nm are predicted to have extraordinarily high strength and stiffness per weight, but have been challenging to fabricate

and test experimentally. Here, we use colloidal synthesis to make ~140 nm length and ~15 nm wall thickness hollow Au-Ag nanoboxes with smooth and rough surfaces. In situ scanning electron

microscope and transmission electron microscope testing of the smooth and rough nanoboxes show them to yield at 130 ± 45 MPa and 96 ± 31 MPa respectively, with significant strain hardening.

A higher strain hardening rate is seen in rough nanoboxes than smooth nanoboxes. Finite element modeling is used to show that the structure of the nanoboxes is not responsible for the

AMORPHOUS ALLOYS Article Open access 20 June 2023 NEAR-THEORETICAL STRENGTH AND DEFORMATION STABILIZATION ACHIEVED VIA GRAIN BOUNDARY SEGREGATION AND NANO-CLUSTERING OF SOLUTES Article Open

access 28 October 2024 CHALLENGING THE IDEAL STRENGTH LIMIT IN SINGLE-CRYSTALLINE GOLD NANOFLAKES THROUGH PHASE ENGINEERING Article Open access 22 January 2025 INTRODUCTION Porous,

nano-architected metals are of interest as lightweight, multifunctional structural materials1,2,3. A major benefit of these nanostructured metals is the ability to use nanoscale size effects

to enhance strength and control deformation4,5. For instance, metallic nanowires can have extraordinary strengths of >6 GPa5,6. Plasticity within these nanostructures is governed by

dislocation nucleation rather than the interactions between dislocations and other microstructural features as seen in bulk metals, which leads to novel deformation mechanisms such as shape

memory effects7. These size-dependent properties can be combined with a 3D structural architecture that has an optimized mechanical response to achieve high strength and stiffness, or other

properties such as a negative Poisson’s ratio. This has been demonstrated using computational modeling8,9, but has not been achieved experimentally. For instance, molecular dynamics

simulations show that architected octet nano-lattices with single-crystalline Cu struts of ~5 nm in size should have a yield strength of ~500 MPa, but these structures cannot yet be

fabricated8. Size effects are significantly important as dimensions approach ~10 nm scale. However, it remains challenging to fabricate architected metals with dimensions down to this order

using current fabrication methods. Porous metals with ordered structural architecture have been fabricated by using polymer templates and subsequent metal deposition using electroplating or

sputtering, but the resulting structures have metal features of ~100 nm to microns in size1,10,11,12. Metal 3D printing is another option for the fabrication of architected metals, but

current methods are limited to ~150 nm features, and restricted to simple geometries without significant overhangs13,14,15. Disordered metallic nano foams are made by electrochemically

dealloying a bimetallic alloy, which results in disordered microstructures with lower specific strength and stiffness than ordered architectures. Nanoscale size effects have previously been

observed in such nano-foams with ligament sizes of 5–100 nm16,17,18,19. These foams have yield strengths of up to ~170 MPa, which indicates that ligaments have strength of ~4.6 GPa. The

ability to create ordered structures at similar length scales should result in further improvements over such disordered structures. Bottom-up colloidal synthesis is a method for making

nano-architected metals that have been widely used in optics, catalysis, and electronics20,21,22. Solid metallic nanocrystals can be synthesized with a range of shapes (e.g. spheres, cubes,

bipyramids, and octahedral) and sizes of 100 nm23,24. These nanocrystals can be transformed into porous nano-architected structures with wall thicknesses down to 5 nm. For instance,

nanoboxes (hollow interior, solid faces) and nanocages (hollow interior, open faces) can be formed from solid cubes. In this way, these colloidal metals combine the ordered structural

architecture and nanoscale dimensions that have been challenging to achieve in top-down structures. It is of interest to determine whether nanoscale size effects can be observed in these

nano-architected metals or if novel deformation mechanisms take place. Hollow spheres made of CdS, carbon, and silica have been found to have high compressive strength25,26,27, but colloidal

metallic nanostructures with complex geometries have not yet been studied. Here, we synthesize ~120–140 nm hollow, cubic Au–Ag nanoboxes with wall thickness of ~15 nm and determine their

mechanical response using in situ scanning electron microscope (SEM) and in situ transmission electron microscope (TEM) compression testing. Smooth and rough nanoboxes are tested to evaluate

the influence of surface roughness on strength and deformation. Smooth nanoboxes are found to have a yield strength of 130 ± 45 MPa, while rough nanoboxes have a yield strength of 96 ± 31 

MPa. Both types of nanoboxes show significant hardening after yield, with rough nanoboxes having a higher hardening rate. Finite element method (FEM) analysis is used to determine the

influence of structural architecture on nanobox deformation and molecular dynamics (MD) simulations are used to understand the atomistic deformation mechanisms responsible for the hardening

behavior. The simulations show that the observed strain hardening is not a result of the structure and geometry of the nanobox, rather, it results from the material’s response involving

accumulation of crystalline defects such as dislocations and stacking faults within the walls of the nanoboxes. RESULTS SYNTHESIS AND CHARACTERIZATION OF AU–AG NANOBOXES Solid Ag nanocubes

with {100} surfaces are synthesized using the polyol-based method28. Hollow nanoboxes are fabricated through galvanic replacement of the solid Ag nanocubes21,29. In the galvanic replacement

reaction, HAuCl4 is added to a solution of Ag nanocubes. HAuCl4 dissociates into H+ and \({\mathrm{AuCl}}_4^ -\) and reacts with the Ag nanocubes in the following reaction30:

$$3{\mathrm{Ag}} + {\mathrm{AuCl}}_4^ - \to {\mathrm{Au}} + 3{\mathrm{Ag}}^ + + 4{\mathrm{Cl}}^ -$$ (1) This reaction results in the removal of Ag and the deposition of Au. Hollow nanoboxes

are obtained from this reaction by Au depositing epitaxially on the surfaces of the Ag nanocube, which blocks further removal of Ag from that region. After this, the removal of Ag occurs at

holes that are formed on the surface of the nanocube. Electrons generated during this galvanic reaction travel to the surface of the nanocube and more Au atoms are deposited on the

surface20,31. The Ag nanocubes used in these experiments are 103 ± 8 nm in length, having rounded corners with radius of curvature of 11 ± 2 nm. A low concentration of HAuCl4 results in

smooth nanoboxes, while a higher concentration results in rough nanoboxes (Fig. 1). The smooth and rough nanoboxes have sizes of 139 ± 9 nm and 121 ± 12 nm, respectively (Fig. 2). Both

smooth and rough nanoboxes contain holes at the corners of the cubes, which has also been observed in previous studies on nanobox20. A nanocube with sharp corners has only {100} facets

exposed but a nanocube with rounded corners has some {111} character at the corners. The {111} facets are poorly passivated in comparison to {100} facets, which results in the preferential

removal of Ag atoms at the corners to create pits that grow into holes20,22,30. The holes at the cube corners have a diameter of 19 ± 4 nm in both the smooth and rough nanoboxes. TEM images

show that the smooth and rough nanoboxes have wall thicknesses of 18 ± 3 nm and 14 ± 4 nm, respectively (Fig. 2). Each rough nanobox also contains 4–5 holes of characteristic diameter of 11 

± 7 nm randomly distributed on the walls, as measured using SEM images. The surface protrusions on the rough nanoboxes are estimated to have a height 10 ± 3 nm using TEM. The nanoboxes

studied here are expected to be single crystalline. Previous studies, that used identical synthetic protocols, have used high-resolution TEM imaging and TEM diffraction to show that hollow

structures formed from Ag nanocubes using galvanic exchange are single crystalline32,33. The resulting nanoboxes contain both Au and Ag, with the rough nanoboxes having a higher ratio of

Au:Ag than the smooth nanoboxes. According to the galvanic exchange reaction (Eq. (1)), three Ag atoms are replaced by one Au atom, which should lead to an overall decrease in solid volume

(volume of the nanobox excluding the hollow interior). By comparing the initial volume of the solid Ag nanocube, and the final volumes of the smooth and rough nanoboxes, we determine that

the galvanic exchange reaction does not go to completion. For instance, the solid volume of the smooth nanoboxes is higher than that of the solid Ag nanocube, which indicates that the smooth

nanoboxes contain both Au and Ag. The rough nanoboxes have ~17% lower volume than the solid Ag nanocubes, which indicates that the rough nanoboxes contain a higher ratio of Au:Ag than the

smooth nanoboxes. This analysis is in agreement with previous energy dispersive spectroscopy (EDS) of hollow nanocubes and rough nanocages, which showed an Au:Ag ratio of 30:70 and 70:30,

respectively34,35. This difference in composition is not expected to cause a significant difference in the properties of the smooth and rough nanoboxes. The Ag and Au interface does not

impede the passage of dislocations or stacking faults, so the difference in composition should not affect the deformation mechanism for the nanoboxes36. IN SITU TESTING OF NANOBOXES The

nanoboxes were compressed using in situ SEM mechanical testing. Nanoboxes are imaged before and after compression testing to determine the change in dimensions during the test. Nanoboxes are

deposited onto a Si wafer and compressed using a diamond flat punch in SEM. The structures are compressed at a constant loading rate of 1 µNs−1 for all samples, which is equivalent to a

strain rate of ~0.01–0.02 s−1, with a 50% strain stopping condition. Ten and eleven compression tests are performed on the smooth and rough nanoboxes, respectively. The compressive

engineering stress-strain curves for both samples show an initial linear loading region followed by yielding (Fig. 3). We define the yield point as the limit of the linear region of the

stress-strain plot. Yielding occurs at 130 ± 45 MPa for the smooth nanoboxes and 96 ± 31 MPa for rough nanoboxes. In the compressive stress-strain curves for the smooth nanocubes, the

initial region is a linear regime up to the yield point. A range of behaviors is observed in the smooth nanoboxes after the yield point. Two samples show a load drop followed by hardening

(blue curve in Fig. 3a). Another sample shows a plateau in stress and then hardening (red curve in Fig. 3a). The remaining samples show hardening after yielding, and increased hardening rate

after 60% strain (black and pink curves in Fig. 3a). In contrast, the majority of the rough nanoboxes show continuous hardening (Fig. 3b). A small plateau after yielding is observed in a

few of the samples (pink curve in Fig. 3b). Despite differences in the shapes of the stress-strain curves, the stress is ~250 MPa at 60% strain for both the smooth and rough nanoboxes,

suggesting that the structural influence on deformation is reduced as the porous structure densifies. The hardening rate of the nanoboxes is quantified using Eq. (2)37: $$\sigma

_{{\mathrm{pl}}} = {\mathrm{K}}\varepsilon ^{\mathrm{n}}$$ (2) Here, K is the strength coefficient, _σ_pl is the plastic stress, _ε_ is the corresponding total strain, and _n_ is the strain

hardening exponent. The strain hardening exponent is found to be 0.3 for the smooth nanoboxes and 0.7 for the rough nanoboxes. This indicates that the rough nanoboxes have a higher hardening

rate than the smooth nanoboxes. In summary, the experimental stress-strain curves for the rough nanoboxes show a lower yield strength and a greater degree of hardening than the smooth

nanoboxes. Although the dimensions of the walls differ between the smooth and the rough nanoboxes, the difference in yield strengths cannot be attributed to nanoscale size effects. The

characteristic length scale of interest in the nanobox is the thickness of the sidewall, as this is the load-bearing structure within the nanobox. The rough nanoboxes have thinner walls than

the smooth nanoboxes. Considering the “smaller is stronger” size effect in nanoscale single-crystalline metals38, the thinner walls should be stronger than the thicker ones, which is not

observed. Other researchers have proposed a size-independent strength when metallic nanostructures are in the 200 nm regime39. This would result in rough nanoboxes with the same strength as

smooth nanoboxes per nanobox cross-sectional (load-bearing) area, which is also not observed. We postulate that the rough protrusions act as stress concentrations that reduce the barrier for

surface defect nucleation. This is explored further using MD simulations and analytical analysis in the following sections. The mechanical response of the hollow nanoboxes is substantially

different from that of solid, single-crystalline metallic nanostructures, but is similar to nano- and micro-porous metal foams, and thin-shelled nanostructures such as carbon

nanotubes17,40,41,42. Single crystalline metallic nanopillars and nanowires tested in compression show a high yield strength of up to 1.5 GPa, jerky plastic flow indicative of dislocation

avalanches and no hardening43,44,45. This behavior has been shown in the solid Ag nanocubes that are used to form the nanoboxes46. In contrast, the hollow nanoboxes deform gradually, without

large slip events, and show significant strain hardening. Metallic foams and thin-shelled nanostructures also have compressive stress-strain curves with gradual deformation, and hardening.

This difference is primarily due to deformation modes such bending and buckling, which are not present in solid single-crystalline nanostructures under uniaxial compression. For instance,

nanoporous gold nanowires of diameter 30–70 nm with ligament sizes 5–10 nm yield at ~100 MPa stress, and show considerable strain hardening beyond the yield point17. Microporous open-cell

metallic foams show a stress drop after yielding, which is followed by strain hardening40,47. This stress-strain response is also observed in individual carbon nanotubes loaded in

compression that deform through shell buckling42. A post compression SEM image of a smooth nanobox shows that it is 32% wider after compression (Fig. 4a), which is larger than the shape

change that is expected from elastic deformation alone. If the load-bearing walls of the nanoboxes were loaded in uniaxial compression up to the yield point and had the properties of solid

Ag nanocubes (yield strength of 637 ± 251 MPa), an estimated nominal yield stress of ~270 MPa is required for the deformation46. This indicates that the nanobox has deformed plastically by a

mode other than uniaxial compression. The compressive yield strength of the load-bearing walls maybe even higher than that of solid Ag nanocubes due to the small width of the walls. For

instance, Ag nanowires with diameters of ~40 nm have been observed to have yield strengths of ~4.5 GPa6. If the walls of the nanoboxes have this high strength, then the nanoboxes can be

expected to have a yield strength of ~2 GPa in uniaxial compression. The measured nanobox yield stress of ~130 MPa is much lower than these estimates, which indicates that another

deformation mode takes place. These results can be compared with in situ TEM compression tests on the nanoboxes, which were performed at a strain rate of ~0.03 s−1. The in situ TEM movie of

nanobox compression (Supplementary Movie 1) shows that the nanobox sidewalls appear to thicken after the nanobox makes contact with the compression plate, and the holes at the corners of the

nanobox become elongated. Lines of dark and bright contrast can be observed on the front/back facing sidewalls, which may correspond to the formation of stacking faults. Comparison of pre-

and post-compression TEM images that were extracted from the in situ TEM movie (Fig. 4 b, c) show a ~10% increase in the width of the nanobox after compression, and no evidence of bending in

the sidewalls. Differences in the post compression in situ SEM and TEM mechanical testing images may be due to differences in strain rate, noise levels, or subtle differences in nanobox

geometry. In addition, the experimental stress-strain curves show a range of behaviors for both the smooth and rough nanoboxes, which may result in different deformation modes. FINITE

ELEMENT MODELING For further insight into the influence of structural architecture on deformation, a hollow smooth nanobox is simulated using FEM analysis. The purpose of this FEM simulation

is to determine the structural response for a material that does not include strain hardening. This is relevant because the solid Ag nanocube (the parent structure from which the nanobox is

formed) does not show strain hardening under compression46. In this way, the FEM simulation reveals the deformation of a hollow box, without consideration of material or size effects. Thus,

an elastic-plastic material model that does not include strain hardening was used in the FEM simulation, to mimic the material response of a Ag single-crystal nanocube46. The FEM model was

then constructed to have a similar geometry as the experimental nanobox, with smooth walls and a hollow interior. The simulated nanobox is deformed in compression, resulting in compression

and bending of the sidewalls. The simulations show high-stress concentrations at the corners of the nanobox and the sidewalls due to bending, relative to the rest of the nanobox (Fig. 5a).

The bending of the sidewalls also contributes to a significant increase in the width of the nanobox. At ~20% strain, the width of the nanobox increases by ~20% (Fig. 5b). The resulting

force-displacement curve is converted into an engineering stress-strain curve by normalizing to the initial footprint of the nanobox (Fig. 5c). This stress-strain curve shows a linear

elastic regime that is followed by yielding at ~230 MPa. After yield, there is a small increase in stress followed by a decrease in stress after 8% strain. This curve shape is also observed

in the uniaxial compression of cylindrical shells, with variations of the curve shape-changing depending on the wall thickness to size ratio48,49. While the structural changes in the

simulated nanobox are qualitatively similar to the experimental nanoboxes (Fig. 4a), FEM analysis does not capture the increase in stress that is observed in both the smooth and rough

nanoboxes after yield. This indicates that the hardening behavior observed in the experimental nanoboxes results from material rather than structural effects. MOLECULAR DYNAMIC SIMULATIONS

The influence of material properties and size effects on deformation mechanisms are investigated using MD simulations. Ag nanoboxes were simulated with a wall thickness to length ratios of

1:7 (similar geometry as the experimental nanoboxes), and an overall size of 50 nm. They are compressed at a force rate of 105 µN/s. Figure 6a–c shows the atomic configuration of a

cross-section of the 1:7 sample at 7%, 23%, and 53% strain. At 7% strain, it can be seen that failure and subsequent plasticity occurred via nucleation of partial dislocations from the outer

and inner surfaces of the nanobox and extended stacking faults (red atoms) that traverse the sidewalls of the nanobox. Several intersections have formed between dislocations that are

nucleated at opposing walls. At 23% strain, dislocation nucleation continues at the top and bottom walls of the nanobox due to a bending moment from the deformation of the sidewalls.

Dislocation density in the sidewalls increases, mainly in the central region. At 53% strain, defects left behind from dislocation slip and interactions including stacking faults and

disordered regions are found throughout the entirety of the sidewalls, and the deformed sidewalls have contacted the top and bottom of the nanobox, which leads to rapidly increasing stress.

Ag nanoboxes with wall thickness to length ratios of 1:16, and 1:25 were also investigated, to determine deformation mechanisms in nanoboxes with more slender sidewalls than the experimental

nanoboxes. Figure 6d, e shows the atomic configuration of a cross-section of the 1:16 and 1:25 sample at 23% strain, respectively. The nucleation and glide of partial dislocations

contribute to deformation in these geometries as well. With decreasing wall thickness, a greater amount of bending is observed in the sidewalls, and fewer of the extended stacking faults

intersect. The observed bending agrees with the post compression SEM image (Fig. 4a), but is not observed in in situ TEM compression (Fig. 4c, and Supplementary Movie 1). This indicates that

the loading state for the in situ SEM test is closer to ideal compression as in MD simulations, while the in situ TEM test may deviate further from ideal conditions. However, a failure of

the sidewall is observed during the in situ TEM video (Supplementary Movie 1), which matches with the failure observed in MD simulations (Fig. 6c). Interfaces such as twin boundaries and

grain boundaries can act as barriers to dislocation motion and contribute to strengthening50. Previous MD simulations subjected nanotwinned Au nanowires to tension and reported significant

strain hardening that was attributed to coherent twin boundaries serving as strong barriers to the glide of leading partial dislocations51. This phenomenon has also been observed in MD

simulations of nanotwinned Cu samples where twin boundaries were observed to have a strong blocking effect on dislocations52. We note that both of these studies employed interatomic

potentials with similar low stacking fault energies, 43.4 mJ/m2 for Au potential51 and 44.42 mJ/m2 Cu potential52 which compares to the stacking fault energies of 6.24 mJ/m253 and 26 mJ/m254

of potentials used in this study. The energy barrier for the transmission of a partial dislocation across a twin boundary has been calculated to be ~4 meV/atom for FCC Au, and independent

of twin size55. The energy barriers for dislocation slip transmission across a twin boundary is reported to be between 199 and 232 mJ/m2, which is similar to the lower bound of the energy

barrier for grain boundary transmission56. Although similar values are not available for FCC Ag, the similarities between Au, Cu, and Ag indicate that the twin boundaries can contribute to

strengthening. However, no full dislocations were observed in any MD compression sample. Despite the presence of extensive partial dislocations, formation of twins was rarely observed.

Incipient twins of 3–4 atomic layers were observed, but deformation twinning was not a dominant deformation mode (Supplementary Fig. 1). In addition, since we stipulate that the nanoboxes

are single crystalline, grain boundary hardening is not an available deformation mechanism. Deformation dominated by dislocation nucleation has also been reported in MD simulations of Cu

ellipsoidal nanoshells57 as well as partial dislocation and stacking fault dominated deformation in Pd nanoshells58. Deformation of the simulated smooth nanobox samples led to the stress

strain-curves shown in Fig. 6f. In each of the samples, initial elastic deformation was followed by a local peak in stress, and then a stress drop that corresponds to the start of

plasticity. All samples then undergo further plastic deformation followed by a rapid increase in stress due to contact between walls of the nanobox. In the stress-strain curve for the 1:7

sample, significant hardening is observed. This is due to extended stacking faults that act as barriers to dislocation motion (Fig. 6a-c). This can form a trapped leading partial dislocation

that exerts a backstress that prevents the nucleation of its trailing partial and other dislocations from the same surface source. This effectively shuts down active nucleation sources and

requires nucleation from new sources for continued plasticity. Such a hardening mechanism is similar to that observed in both experiments and simulations of nanoporous Au17,59,60,61. Less

hardening is observed in the 1:16 sample, and no hardening is observed in the 1:25 sample. There are fewer dislocations in these samples with more slender sidewalls, which provides further

evidence that hardening is due to the proposed mechanism in which stacking faults impede dislocation glide. Strain-hardening exponents were not computed for the generated MD stress-strain

data. The high strain-rate of the simulated samples results in a much larger yield stress (and consequently overall stress level) than experiments, such that the simulated and experimental

hardening rates cannot be quantitatively compared. The effect of surface roughness on nanobox deformation and failure was also studied using MD simulation. Hemispherical protrusions of 5 nm

diameter were added to the smooth nanobox to construct the rough nanobox (see Supplementary Fig. 2). The most notable difference between the stress-strain curves of the rough and smooth

samples is a significant decrease in yield strength in the rough sample, suggesting a stress concentration factor of ~2. Both samples yield via partial dislocation nucleation from the

surface. This suggests that the protrusions act to promote nucleation of dislocations, likely as stress concentrators. After an initial regime of negligible hardening, the simulated rough

samples display hardening rates similar to the simulated smooth samples, which agrees with experiment. We note that the particular choice of protrusion distribution does not result in

contact between protrusions during compression. The MD results are reasonable when compared with the expected stress concentrations from geometric considerations. Stress concentration

estimated using classical mechanics equations for cylindrical shafts on a surface with fillet radius of curvatures ranging between 1–3 nm at the base and shaft diameters ~10 nm give a

distribution of stress concentration factors of ~1.5862. Experimental yield strengths of rough and smooth nanoboxes indicate a stress concentration factor of ~1.35, which is within the range

of the estimate. The presences of bumps and notches can increase surface areas and alter the corresponding surface free energy. However, previous MD simulations performed on tensile testing

of Silicon nanowires with notched rough surface also show that surface roughness stress concentrations dominate the yield strength over altered surface free energy63. In addition, no strain

hardening is observed in these tensile loaded wires. In conclusion, Au–Ag nanoboxes were compressed using in situ SEM and TEM uniaxial compression testing. Smooth nanoboxes were found to

yield at 130 ± 45 MPa, and rough nanoboxes were found to yield at ~96 ± 31 MPa. Both types of nanoboxes show significant hardening after yield, but the rough nanoboxes have a higher

hardening rate. FEM simulations showed that the nanobox structural geometry does not lead to hardening. Based on MD simulations, we attribute the appearance of strain hardening in our

experimental results to the structures’ material response involving accumulation of crystalline defects such as dislocations and stacking faults within the walls of the nanoboxes. These

results demonstrate the ability to simultaneously control yield strength and hardening by changing sample dimensions, while maintaining the same structural geometry. The mechanical

properties of the nanoboxes indicate that they could be used as components of larger, hierarchical materials, which could be achieved through colloidal self-assembly. It would also be of

interest to study nanoboxes with a range of wall thicknesses, in order to determine transitions in deformation mechanisms at extremely small sizes where dislocations no longer control

mechanical properties. METHODS NANOBOX SYNTHESIS AND STRUCTURAL CHARACTERIZATION AgNO3 (>99.9%, Fisher Scientific), Ethylene glycol (EG, Cl <5 ppm, and Fe <0.2 ppm, Macron Fine

Chemicals), polyvinylpyrrolidone (PVP, Molecular weight of 55 000 g/mol, Sigma Aldrich), and HCl (37%, Fisher Scientific), are used in the polyol synthesis of solid Ag nanocubes. HAuCl4

(>99.9%, Fisher Scientific) is used in the galvanic replacement reaction to form hollow nanoboxes. Ag nanocubes are synthesized in EG. PVP is used as a surfactant. Solutions of 200 mM

AgNO3 in EG and 120 mM PVP in EG are prepared by sonication. A total of 60 mM HCl in EG is prepared by dissolving 4.9 µl of 37% HCl in 1 ml of EG. 1 ml of EG is heated in a 22 ml vial

submerged in a mineral oil bath at 137 °C for 20 min partially covering the mouth with the cap. A total of 50 µl of HCl, 1 ml of the prepared AgNO3 and 1 ml PVP solutions are added and the

cap is closed when the reaction solution turns pink. The reaction is left at 137 °C for 2.5 h before the seeding starts, after which the reaction completes within 15–20 min resulting in a

yellowish-green solution color. A total of 500 ml of the prepared Ag nanocubes are cleaned using centrifugation once with 2X amount of acetone to remove EG and three times with water to

remove excess surfactant at 2500 rpm for 7 min and resuspended in 100 µl of water for further use in galvanic replacement. A total of 100 µl of the cleaned Ag nanocubes are slowly reacted

with 1.5 ml of 1 mM HAuCl4 added drop wise over 30 min to obtain smooth Au–Ag nanoboxes with corner pits of 19 ± 4 nm diameter. Another batch of 100 µl of Ag nanocubes is reacted with 2.5 ml

of HAuCl4 added dropwise in 25 min to obtain the roughened Au nanoboxes. Both the samples are cleaned three times with water at 2500 rpm for 5 min to remove excess surfactant. Cleaned

samples are deposited on silicon wafer for SEM imaging and in situ compressions as well as TEM grid for characterization (Fig. 2). SEM and bright field TEM imaging are used to characterize

the samples for their lengths, wall thickness, and surface roughness. TEM images were obtained on an FEI Tecnai G2 F20 X-TWIN TEM at 200 kV. FEI Helios NanoLab 600i DualBeam FIB/SEM is used

to obtain SEM images for pre compression and post compression characterization. ImageJ is used to calculate particle sizes, wall thickness, roughness and hole sizes, etc. from the SEM and

TEM images. The values reported are the average of measured sizes with the standard deviation of the set as +/– bounds. MECHANICAL TESTING In situ SEM mechanical testing was performed with

the Nanoflip in situ mechanical tester (Nanomechanics, Inc.) inside of a FEI Helios NanoLab 600i DualBeam FIB/SEM. The nanoboxes were compressed at a constant loading rate of 1 µN/s with a

1000 Hz data acquisition rate. Nanoboxes were compressed up to ~60% strain. Force displacement curves were corrected for frame stiffness. Engineering stress and strain were computed by

dividing the corrected force and displacement by the nominal (footprint) area and length of the structure, respectively. The strain hardening exponents were obtained by fitting an

exponential relation of _σ_ = _Kε__n_ to post-yield experimental data for each individual test curve. The values of _n_ from all tests were then averaged to get the reported values. The

densification stage was not taken in the curve fitting as this sharp rise in stress is due to touching sidewalls and not the material strain hardening effect. The fitting was limited up to

50% strain. The values of yield stress and strain hardening exponent reported are the average of measured sizes with the standard deviation of the set as +/– bounds. In situ TEM compression

testing was performed at the Center for Integrated Nanotechnologies, Sandia National Laboratories using a PI-95 nanoindenter (Bruker Inc.) in a JEOL 2100 TEM at 200 kV. Hollow Ag nanocubes

were dropcast onto a 1 μm plateau Si wedge and compressed at a strain rate of 0.03 1/s. FINITE ELEMENT MODELING A 3D model of the hollow nanobox was created in SolidWorks, and then exported

to Abaqus/CAE 2018. The nanobox was seeded at the edges with a global spacing of 7 and then meshed with tetrahedral elements, resulting in over 400,000 nodes and 200,000 elements. An

isotropic and anisotropic elastic perfectly plastic material model was used. For the isotropic model, an elastic modulus and yield strength of 47 GPa and 600 MPa were used, respectively,

which were derived from Ag <100> properties. For the anisotropic model, the elastic stiffness matrix was populated using c11, c12, and c44 constants for silver of 124, 93.4, and 46.1 

GPa, respectively (See Supplementary Methods – FEM simulation)64. The nanobox was placed between a rigid bottom plate that was fixed in all degrees of freedom and a rigid top plate that was

only allowed to move in the z-direction (loading direction). Load was applied normal to the top plate to simulate compression. The static Riks (or arc length) method was used to account for

the possibility of negative or near-zero stiffness during compression. MOLECULAR DYNAMICS SIMULATIONS MD simulation samples were constructed by starting with a solid cube of Ag atoms with

dimensions of 50 nm and {100} faces. Interior atoms were removed to achieve desired wall thickness to length aspect ratios. For all geometries, a 7 nm wide cube was removed from each of the

corners of the simulated hollow nanobox (Supplementary Fig. 3). Before compression, all samples were subjected to energy minimization and thermal relaxation. The total potential energy of

the initial sample configuration was minimized following a conjugate gradient scheme allowing the atomic positions to relax. The system was then assigned a velocity profile corresponding to

300 K and the samples were thermally equilibrated under time integration of the NVT ensemble for 200 ps. The samples were then equilibrated for an additional 200 ps using Langevin dynamics

in order to dampen the pressure oscillations caused by rapid application of temperature. Compression was applied to the simulated nanoboxes using a force-controlled scheme by creating two

stiff Si plates above and below the nanobox. The Ag-Si interaction used to simulate the interaction between the compression plates and the nanobox was assumed to be of a Lennard-Jones 6–12

type with interaction parameters from Ngandjong et al.65. During compression, the bottom plate is held fixed while the top plate is subjected to a constant force rate. In order to

investigate the rate effect in simulated compression, we subjected all nanobox samples to force rates of 105, 106, 107, and 108 µN/s (Supplementary Fig. 4). Minimal differences in both the

output atomic configurations and the stress-strain data between the 106 µN/s and 105 µN/s simulations indicate that rate effects are minimized in the 105 µN/s. We, therefore, report the

results of the lowest force rate 105 µN/s in the manuscript. Simulated compression was performed until >80% strain unless non-physical behavior was observed in the atomic output, in which

case the simulation was halted. Interactions between Ag atoms were modelled using the embedded atom method (EAM) and implemented using a potential developed by Foiles et al.53. In order to

check the validity of this Ag potential, we repeated compression simulations using an Ag potential from Sheng, et al. which was fit to a different set of physical properties including the

stable and unstable stacking fault energies54. The Foiles potential resulted in values of 6.24 mJ/m2 and 116 mJ/m2, and the Sheng potential resulted in values of 26 mJ/m2 and 114 mJ/m2 for

stable and unstable stacking fault energies, respectively. Quantitatively, the stress-strain curves generated using both potentials and the resulting atomic deformation mechanisms are

similar (Supplementary Fig. 5). This shows that the Foiles potential can capture the relevant deformation behavior in the Ag nanoboxes, which are the simulations that are shown in the

manuscript. All simulations were performed using the LAMMPS molecular dynamics software66 using a timestep of 1 fs and OVITO67 was used for common neighbor analysis (CNA) and visualization

of atomic configurations. To calculate the stress in the simulated nanobox, we relate engineering stress to the atomic quantities that are computed during MD simulations. For compression

aligned along the _z_-axis, stress is determined as shown in below equation: $$\sigma _{zz} = \frac{{F_z}}{{{\mathrm{A}}_0}} = \frac{{{\sum} {\upsilon s_{{\mathrm{zz}}}}

/{{L}}_{{z}}}}{{{{L}}_{{\mathrm{x}}0}{{L}}_{{\mathrm{y}}0}}}$$ (3) where _L_x0 and _L_y0 are the initial cross-sectional dimensions of the nanobox, _L_z is the height of the nanobox, _υ_ is

the atomic volume, _s_zz is the atomic stress and the summation is over all nanobox atoms. The product, _υs__zz_, can be computed for each nanobox atom following standard definitions68. _L_z

is taken as the separation distance between the two rigid plates and _L_x0 and _L_y0 are computed at the beginning of the simulation using the extrema atomic positions. This form was chosen

to most closely match the computation of engineering stress in experiments. The numerator in Eq. (3) uses the standard calculation of virial stress using the instantaneous sample

configuration and is analogous to the instantaneous force as measured during compression experiments. In order to match the experimental calculation of engineering stress, we then divide by

the initial cross-sectional area of the nanobox. DATA AVAILABILITY The data that support the findings of this study are available from the corresponding author upon reasonable request.

REFERENCES * Schaedler, T. A. et al. Ultralight metallic microlattices. _Science_ 334, 962–965 (2011). Article  ADS  CAS  PubMed  Google Scholar  * Bauer, J. et al. Nanolattices: an emerging

class of mechanical metamaterials. _Adv. Mater._ 29, 1701850 (2017). Article  CAS  Google Scholar  * Schaedler, T. A. & Carter, W. B. Architected cellular materials. _Annu. Rev. Mater.

Res._ 46, 187–210 (2016). Article  ADS  CAS  Google Scholar  * Greer, J. R., Oliver, W. C. & Nix, W. D. Size dependence of mechanical properties of gold at the micron scale in the

absence of strain gradients. _Acta Mater._ 53, 1821–1830 (2005). Article  CAS  Google Scholar  * Wu, B., Heidelberg, A. & Boland, J. J. Mechanical properties of ultrahigh-strength gold

nanowires. _Nat. Mater._ 4, 525–529 (2005). Article  ADS  CAS  PubMed  Google Scholar  * Filleter, T. et al. Nucleation-controlled distributed plasticity in penta-twinned silver nanowires.

_Small_ 8, 2986–2993 (2012). Article  CAS  PubMed  Google Scholar  * Liang, W., Zhou, M. & Ke, F. Shape memory effect in Cu nanowires. _Nano Lett._ 5, 2039–2043 (2005). Article  ADS  CAS

  PubMed  Google Scholar  * He, Z., Wang, F., Zhu, Y., Wu, H. & Park, H. S. Mechanical properties of copper octet-truss nanolattices. _J. Mech. Phys. Solids_ 101, 133–149 (2017). Article

  ADS  CAS  Google Scholar  * Sha, Z. D. et al. Metallic glass-based chiral nanolattice: light weight, auxeticity, and superior mechanical properties. _Mater. Today_ 20, 569–576 (2017).

Article  CAS  Google Scholar  * Zheng, X. et al. Multiscale metallic metamaterials. _Nat. Mater._ 15, 1100–1106 (2016). Article  ADS  CAS  PubMed  Google Scholar  * Wendy, Gu,X. & Greer,

J. R. Ultra-strong architected Cu meso-lattices. _Extrem. Mech. Lett._ 2, 7–14 (2015). Article  Google Scholar  * do Rosário, J. J. et al. Self-assembled ultra high strength, ultra stiff

mechanical metamaterials based on inverse opals. _Adv. Eng. Mater._ 17, 1420–1424 (2015). Article  CAS  Google Scholar  * Ladd, C., So, J.-H., Muth, J. & Dickey, M. D. 3D printing of

free standing liquid metal microstructures. _Adv. Mater._ 25, 5081–5085 (2013). Article  CAS  PubMed  Google Scholar  * Reiser, A. et al. Multi-metal electrohydrodynamic redox 3D printing at

the submicron scale. _Nat. Commun._ 10, 1853 (2019). Article  ADS  PubMed  PubMed Central  CAS  Google Scholar  * Saleh, M. S., Hu, C. & Panat, R. Three-dimensional microarchitected

materials and devices using nanoparticle assembly by pointwise spatial printing. _Sci. Adv._ 3, e1601986 (2017). Article  ADS  PubMed  PubMed Central  CAS  Google Scholar  * Biener, J.,

Hodge, A. M., Hamza, A. V., Hsiung, L. M. & Satcher, J. H. Nanoporous Au: a high yield strength material. _J. Appl. Phys._ 97, 024301 (2005). Article  ADS  CAS  Google Scholar  * Dou, R.

& Derby, B. Deformation mechanisms in gold nanowires and nanoporous gold. _Philos. Mag._ 91, 1070–1083 (2011). Article  ADS  CAS  Google Scholar  * Biener, J. et al. Size Effects on the

Mechanical Behavior of Nanoporous Au. _Nano Lett._ 6, 2379–2382 (2006). Article  ADS  CAS  PubMed  Google Scholar  * Hodge, A. M. et al. Scaling equation for yield strength of nanoporous

open-cell foams. _Acta Mater._ 55, 1343–1349 (2007). Article  CAS  Google Scholar  * Skrabalak, S. E. et al. Gold nanocages: synthesis, properties, and applications. _Acc. Chem. Res._ 41,

1587–1595 (2008). Article  CAS  PubMed  PubMed Central  Google Scholar  * Skrabalak, S. E., Au, L., Li, X. & Xia, Y. Facile synthesis of Ag nanocubes and Au nanocages. _Nat. Protoc._ 2,

2182–2190 (2007). Article  CAS  PubMed  Google Scholar  * Chen, J. et al. Facile synthesis of gold−silver nanocages with controllable pores on the surface. _J. Am. Chem. Soc._ 128,

14776–14777 (2006). Article  CAS  PubMed  PubMed Central  Google Scholar  * Xia, Y., Xiong, Y., Lim, B. & Skrabalak, S. E. Shape-controlled synthesis of metal nanocrystals: simple

chemistry meets complex physics? _Angew. Chem. Int. Ed._ 48, 60–103 (2009). Article  CAS  Google Scholar  * Xia, Y., Xia, X., Wang, Y. & Xie, S. Shape-controlled synthesis of metal

nanocrystals. _MRS Bull._ 38, 335–344 (2013). Article  CAS  Google Scholar  * Shan, Z. W. et al. Ultrahigh stress and strain in hierarchically structured hollow nanoparticles. _Nat. Mater._

7, 947–952 (2008). Article  ADS  CAS  PubMed  Google Scholar  * Yang, W. et al. Large-deformation and high-strength amorphous porous carbon nanospheres. _Sci. Rep._ 6, 24187 (2016). Article

  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Zhang, L. et al. Hollow silica spheres: synthesis and mechanical properties. _Langmuir_ 25, 2711–2717 (2009). Article  CAS  PubMed 

Google Scholar  * Jeon, S.-J., Yazdi, S., Thevamaran, R. & Thomas, E. L. Synthesis of monodisperse single crystalline Ag microcubes via seed-mediated growth. _Cryst. Growth Des._ 17,

284–289 (2017). Article  CAS  Google Scholar  * Sun, Y. & Xia, Y. Mechanistic study on the replacement reaction between silver nanostructures and chloroauric acid in aqueous medium. _J.

Am. Chem. Soc._ 126, 3892–3901 (2004). Article  CAS  PubMed  Google Scholar  * Lu, X. et al. Mechanistic studies on the galvanic replacement reaction between multiply twinned particles of Ag

and HAuCl4 in an organic medium. _J. Am. Chem. Soc._ 129, 1733–1742 (2007). Article  CAS  PubMed  PubMed Central  Google Scholar  * González, E., Arbiol, J. & Puntes, V. F. Carving at

the nanoscale: sequential galvanic exchange and Kirkendall growth at room temperature. _Science_ 334, 1377–1380 (2011). Article  ADS  PubMed  CAS  Google Scholar  * Hong, X., Wang, D., Cai,

S., Rong, H. & Li, Y. Single-crystalline octahedral Au–Ag nanoframes. _J. Am. Chem. Soc._ 134, 18165–18168 (2012). Article  CAS  PubMed  Google Scholar  * Sun, Y., Mayers, B. T. &

Xia, Y. Template-Engaged Replacement Reaction: A One-Step Approach to the Large-Scale Synthesis of Metal Nanostructures with Hollow Interiors. _Nano Lett._ 2, 481–485 (2002). Article  ADS 

CAS  Google Scholar  * Lu, X. et al. Fabrication of cubic nanocages and nanoframes by dealloying Au/Ag alloy nanoboxes with an aqueous etchant based on Fe(NO3)3 or NH4OH. _Nano Lett._ 7,

1764–1769 (2007). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  * Gilroy, K. D., Sundar, A., Farzinpour, P., Hughes, R. A. & Neretina, S. Mechanistic study of

substrate-based galvanic replacement reactions. _Nano Res._ 7, 365–379 (2014). Article  CAS  Google Scholar  * Kiani, M. T., Wang, Y., Bertin, N., Cai, W. & Gu, X. W. Strengthening

mechanism of a single precipitate in a metallic nanocube. _Nano Lett._ 19, 255–260 (2019). Article  ADS  CAS  PubMed  Google Scholar  * Combaz, E. & Mortensen, A. Fracture toughness of

Al replicated foam. _Acta Mater._ 58, 4590–4603 (2010). Article  CAS  Google Scholar  * Greer, J. R. & De Hosson, J. T. M. Plasticity in small-sized metallic systems: Intrinsic versus

extrinsic size effect. _Prog. Mater. Sci._ 56, 654–724 (2011). Article  CAS  Google Scholar  * Han, W.-Z. et al. From “smaller is stronger” to “size-independent strength plateau”: towards

measuring the ideal strength of iron. _Adv. Mater._ 27, 3385–3390 (2015). Article  CAS  PubMed  Google Scholar  * Zhou, J. & Soboyejo, W. O. Compression–compression fatigue of open cell

aluminum foams: macro-/micro- mechanisms and the effects of heat treatment. _Mater. Sci. Eng. A_ 369, 23–35 (2004). Article  CAS  Google Scholar  * Dong, L., Deshpande, V. & Wadley, H.

Mechanical response of Ti–6Al–4V octet-truss lattice structures. _Int. J. Solids Struct._ 60–61, 107–124 (2015). Article  CAS  Google Scholar  * Waters, J. F. et al. Shell buckling of

individual multiwalled carbon nanotubes using nanoindentation. _Appl. Phys. Lett._ 87, 103109 (2005). Article  ADS  CAS  Google Scholar  * Seo, J.-H. et al. Superplastic deformation of

defect-free Au nanowires via coherent twin propagation. _Nano Lett._ 11, 3499–3502 (2011). Article  ADS  CAS  PubMed  Google Scholar  * Seo, J.-H. et al. Origin of size dependency in

coherent-twin-propagation-mediated tensile deformation of noble metal nanowires. _Nano Lett._ 13, 5112–5116 (2013). Article  ADS  CAS  PubMed  Google Scholar  * Greer, J. R. & Nix, W. D.

Nanoscale gold pillars strengthened through dislocation starvation. _Phys. Rev. B_ 73, 245410 (2006). Article  ADS  CAS  Google Scholar  * Kiani, M. T., Patil, R. P. & Gu, X. W.

Dislocation surface nucleation in surfactant-passivated metallic nanocubes. _MRS Commun._ 9, 1029–1033 (2019). Article  CAS  Google Scholar  * Goel, M. D. et al. Dynamic compression behavior

of cenosphere aluminum alloy syntactic foam. _Mater. Des._ 42, 418–423 (2012). Article  ADS  CAS  Google Scholar  * Gorbachov, A., Stranghöner, N. & Rotter, J. M. Buckling behaviour of

axially compressed cylindrical shells made of stainless steel. _ce/Pap._ 1, 828–837 (2017). Article  Google Scholar  * Batterman, S. C. Plastic buckling of axially compressed cylindrical

shells. _AIAA J._ 3, 316–325 (1965). Article  ADS  MATH  Google Scholar  * Lu, K., Lu, L. & Suresh, S. Strengthening materials by engineering coherent internal boundaries at the

nanoscale. _Sci. (80-.)_ 324, 349–352 (2009). Article  ADS  CAS  Google Scholar  * Deng, C. & Sansoz, F. Enabling ultrahigh plastic flow and work hardening in twinned gold nanowires.

_Nano Lett._ 9, 1517–1522 (2009). Article  ADS  CAS  PubMed  Google Scholar  * Wu, Z. X., Zhang, Y. W. & Srolovitz, D. J. Dislocation–twin interaction mechanisms for ultrahigh strength

and ductility in nanotwinned metals. _Acta Mater._ 57, 4508–4518 (2009). Article  CAS  Google Scholar  * Foiles, S. M., Baskes, M. I. & Daw, M. S. Embedded-atom-method functions for the

fcc metals Cu, Ag, Au, Ni, Pd, Pt, and their alloys. _Phys. Rev. B_ 33, 7983–7991 (1986). Article  ADS  CAS  Google Scholar  * Sheng, H. W., Kramer, M. J., Cadien, A., Fujita, T. & Chen,

M. W. Highly optimized embedded-atom-method potentials for fourteen fcc metals. _Phys. Rev. B_ 83, 134118 (2011). Article  ADS  CAS  Google Scholar  * Wang, J., Cao, G., Zhang, Z. &

Sansoz, F. Size-dependent dislocation–twin interactions. _Nanoscale_ 11, 12672–12679 (2019). Article  CAS  PubMed  Google Scholar  * Sangid, M. D., Ezaz, T. & Sehitoglu, H. Energetics of

residual dislocations associated with slip–twin and slip–GBs interactions. _Mater. Sci. Eng. A_ 542, 21–30 (2012). Article  CAS  Google Scholar  * Yang, Q., Yang, Z., Yang, Y., Zhang, G.

& Zhang, Y. Mechanical properties of single crystal copper ellipsoidal nanoshells by molecular dynamics. _Int. J. Mod. Phys. B_ 32, 1850196 (2018). Article  ADS  CAS  Google Scholar  *

Valencia, F. J. et al. Mechanical properties obtained by indentation of hollow Pd nanoparticles. _J. Phys. Chem. C._ 122, 25035–25042 (2018). Article  CAS  Google Scholar  * Abdolrahim, N.

et al. The mechanical response of core-shell structures for nanoporous metallic materials. _Philos. Mag._ 93, 736–748 (2013). Article  ADS  CAS  Google Scholar  * Ruestes, C. J., Farkas, D.,

Caro, A. & Bringa, E. M. Hardening under compression in Au foams. _Acta Mater._ 108, 1–7 (2016). Article  CAS  Google Scholar  * Ngô, B.-N. D. et al. Anomalous compliance and early

yielding of nanoporous gold. _Acta Mater._ 93, 144–155 (2015). Article  CAS  Google Scholar  * Pilkey, W. D. Formulas for Stress, Strain, and Structural Matrices: Second Edition. (Wiley,

2005). https://doi.org/10.1002/9780470172681. * Liu, Q., Wang, L. & Shen, S. Effect of surface roughness on elastic limit of silicon nanowires. _Comput. Mater. Sci._ 101, 267–274 (2015).

Article  CAS  Google Scholar  * Bower, A. F. _Applied mechanics of solids_. (CRC Press, Taylor and Francis Group, 2010). * Ngandjong, A. C., Mottet, C. & Puibasset, J. Freezing and

melting of silver nanoparticles on silica substrate using a simple interatomic potential for Ag–SiO 2 interaction on the basis of ab initio calculations and experimental data. _J. Phys.

Chem. C._ 121, 3615–3622 (2017). Article  CAS  Google Scholar  * Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. _J. Comput. Phys._ 117, 1–19 (1995). Article  ADS 

CAS  MATH  Google Scholar  * Stukowski, A. Visualization and analysis of atomistic simulation data with OVITO–the open visualization tool. _Model. Simul. Mater. Sci. Eng._ 18, 015012 (2009).

Article  ADS  Google Scholar  * Thompson, A. P., Plimpton, S. J. & Mattson, W. General formulation of pressure and stress tensor for arbitrary many-body interaction potentials under

periodic boundary conditions. _J. Chem. Phys._ 131, 154107 (2009). Article  ADS  PubMed  CAS  Google Scholar  Download references ACKNOWLEDGEMENTS We gratefully acknowledge financial support

from the Stanford SystemX Alliance. M.T.K. is supported by the National Defense and Science Engineering Graduate Fellowship. D.D. is supported by the National Science Foundation Graduate

Research Fellowship under Grant No. 1656518. C.M.B. and K.H. time was fully supported by the Division of Materials Science and Engineering, Office of Basic Energy Sciences, U.S. Department

of Energy. Part of this work was performed at the Stanford Nano Shared Facilities (SNSF), which is supported by the National Science Foundation under award ECCS-1542152. This work was

performed, in part, at the Center for Integrated Nanotechnologies, an Office of Science User Facility operated for the U.S. Department of Energy (DOE) Office of Science. Sandia National

Laboratories is a multimission laboratory managed and operated by National Technology & Engineering Solutions of Sandia, LLC, a wholly owned subsidiary of Honeywell International, Inc.,

for the U.S. DOE’s National Nuclear Security Administration under contract DE-NA-0003525. The views expressed in the article do not necessarily represent the views of the U.S. DOE or the

United States Government. We thank Prof. Ill Ryu for insightful discussion regarding underlying mechanisms in rough nanobox deformations. We gratefully acknowledge the financial support from

the Agency for Science, Technology and Research (A*STAR) under grant AMDM A1898b0043, and the use of computing resources at the A*STAR Computational Resource Centre, Singapore. AUTHOR

INFORMATION AUTHORS AND AFFILIATIONS * Department of Mechanical Engineering, Stanford University, Stanford, CA, 94305, USA Radhika P. Patil, David Doan & X. Wendy Gu * Institute of High

Performance Computing, A*STAR, 1 Fusionopolis Way, #16-16 Connexis, Singapore, 138632, Singapore Zachary H. Aitken, Shuai Chen & Yong-Wei Zhang * Department of Materials Science and

Engineering, Stanford University, Stanford, CA, 94305, USA Mehrdad T. Kiani * Materials, Physical, and Chemical Sciences, Sandia National Laboratories, Albuquerque, NM, 87185, USA

Christopher M. Barr & Khalid Hattar Authors * Radhika P. Patil View author publications You can also search for this author inPubMed Google Scholar * David Doan View author publications

You can also search for this author inPubMed Google Scholar * Zachary H. Aitken View author publications You can also search for this author inPubMed Google Scholar * Shuai Chen View author

publications You can also search for this author inPubMed Google Scholar * Mehrdad T. Kiani View author publications You can also search for this author inPubMed Google Scholar * Christopher

M. Barr View author publications You can also search for this author inPubMed Google Scholar * Khalid Hattar View author publications You can also search for this author inPubMed Google

Scholar * Yong-Wei Zhang View author publications You can also search for this author inPubMed Google Scholar * X. Wendy Gu View author publications You can also search for this author

inPubMed Google Scholar CONTRIBUTIONS R.P.P. and X.W.G. designed the study. R.P.P. synthesized the nanostructures, R.P.P. and M.T.K. and conducted in situ SEM mechanical tests, M.T.K. imaged

the nanostructures for characterization, M.T.K. conducted in situ TEM tests with C.M.B. and K.H., R.P.P. and X.W.G. analyzed the experimental data, D.D. performed the finite element

modelling, Z.H.A., S.C. and Y.W.Z. performed the molecular dynamics simulations. R.P.P. wrote the manuscript under supervision of X.W.G. with contribution from co-authors for corresponding

sections. CORRESPONDING AUTHOR Correspondence to X. Wendy Gu. ETHICS DECLARATIONS COMPETING INTERESTS The authors declare no competing interests. ADDITIONAL INFORMATION PEER REVIEW

INFORMATION _Nature Communications_ thanks Eduardo Bringa, Niaz Abdolrahim and the other anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports

are available. PUBLISHER’S NOTE Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. SUPPLEMENTARY INFORMATION SUPPLEMENTARY

INFORMATION PEER REVIEW FILE DESCRIPTION OF ADDITIONAL SUPPLEMENTARY FILES SUPPLEMENTARY MOVIE 1 RIGHTS AND PERMISSIONS OPEN ACCESS This article is licensed under a Creative Commons

Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original

author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the

article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use

is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

http://creativecommons.org/licenses/by/4.0/. Reprints and permissions ABOUT THIS ARTICLE CITE THIS ARTICLE Patil, R.P., Doan, D., Aitken, Z.H. _et al._ Hardening in Au-Ag nanoboxes from

stacking fault-dislocation interactions. _Nat Commun_ 11, 2923 (2020). https://doi.org/10.1038/s41467-020-16760-1 Download citation * Received: 22 August 2019 * Accepted: 22 May 2020 *

Published: 10 June 2020 * DOI: https://doi.org/10.1038/s41467-020-16760-1 SHARE THIS ARTICLE Anyone you share the following link with will be able to read this content: Get shareable link