ABSTRACT On-surface mass transport is the key process determining the kinetics and dynamics of on-surface reactions, including the formation of nanostructures, catalysis, or surface

cleaning. Volatile organic compounds (VOC) localized on a majority of surfaces dramatically change their properties and act as reactants in many surface reactions. However, the fundamental

question “How far and how fast can the molecules travel on the surface to react?” remains open. Here we show that isoprene, the natural VOC, can travel ~1 μm s−1, i.e., centimeters per day,

quickly filling low-concentration areas if they become locally depleted. We show that VOC have high surface adhesion on ceramic surfaces and simultaneously high mobility providing a steady

ACCELERATED BY GAS MOLECULE TUNNELLING-LIKE EFFECT Article 26 May 2022 THE COMPOSITIONAL HOMOGENEITY OF THE METAL PARTICLE DURING VAPOR–LIQUID–SOLID GROWTH OF NANOWIRES Article Open access

06 July 2020 INTRODUCTION On-surface mass transport is the key process determining the kinetics and dynamics of on-surface reactions, including the formation of nanostructures, catalysis, or

surface cleaning1,2,3,4. Volatile organic compounds (VOC) localized on a majority of surfaces greatly impact material properties5,6, complicate the correct material characterization7,8,

should be considered when designing fabrication protocols9, and are an important class of compounds affecting human health within indoor environments10,11,12. The presence of VOC is

typically referred to as contamination that impacts the performance of manufactured semiconductor devices11,12,13, alters metal work function6 and subsequent energy level alignment with

organic semiconductors5,14,15, and other surface properties of metals or ceramics like adhesion, surface free energy, hydrophobicity and biocompatibility16,17,18. Removal of the VOC is

easily possible by plasma or thermal treatments; however, within several minutes to hours, an organic layer is present again on common inorganic surfaces19. Mobility of the VOC is widely

discussed, but the discussion is focused on adsorption and transport by air20,21. On the other hand, the presence of VOC is reported as a source of contamination during electron microscopies

(SEM, TEM) when transport by the atmosphere is restricted22. There, the contamination is visible in areas exposed to the e-beam as the beam changes the chemical composition of VOC23. The

capability of the e-beam to induce chemical reactions is widely employed for the fabrication of nanostructures from organic precursors either by crosslinking or breaking polymer chains in

electron e-beam lithography24 or precursor decomposition in focused electron-beam-induced deposition (FEBID)25,26. The electrons with a low energy of 2.5–100 eV can induce crosslinking of

self-assembled monolayers via electron impact ionization and dissociative electron attachment mechanisms27. Significant changes also occur on surfaces of materials without intentional

exposure to resist films or reactive gas28 due to the presence of native carbon contaminations on surfaces of most common inorganic materials, which can be traced back to VOC origin6. The

polymeric layers formed of surfaces exposed by electrons28,29 lower contrast, enhance electron attenuation in electron spectroscopies, and largely change the properties of surface areas

measured after focused beam milling/deposition was performed7,8,30,31. Indoor environments have surface area-to-volume ratios hundreds of times higher than outdoor environments11,32. The

high surface-to-volume ratio means that surface chemistry impacts indoor air as surfaces adsorb and emit organic molecules and provide the environment for various chemical reactions to take

place10,11,12,32. The thermodynamic and kinetic parameters of VOC adsorption are important inputs for models that include surface physical and chemical processes in the form of deposition

and subsequent removal of compounds or organic film growth10,32. Mass transport of the adsorbed species is an indispensable part of these models because, especially at low partial pressures

of the reactants, surface diffusion is the key process determining the kinetics and dynamics of on-surface reactions1,2,3,4. The significance of surface diffusion in electron beam

transformation of adsorbed organic molecules was established already few decades ago33. Since then, the electron beam writing process has been investigated28,29,31,34,35,36,37,38, and the

essential role of surface diffusion has been confirmed28,29,37,38. In the related field of FEBID, in which the precursor molecules are injected on purpose, the surface diffusion of

precursors can significantly enhance the growth rates by replenishing the consumed monomers26. Reliable diffusion coefficients are necessary for a quantitative description of surface

diffusion. While these are better established on metal surfaces, the quantitative information on diffusion coefficients is rather scarce on oxides. Here we provide a quantitative answer to

the fundamental question: “How far and how fast can the molecules travel on the surface to react?” We have determined the diffusion flow rates of prototypical VOC, isoprene

(2-methyl-1,3-butadiene)39, on the zirconium oxide surfaces. We show that the flow provides a steady supply of reactants for spatially localized on-surface reaction, in our instance,

electron beam (e-beam in following) induced polymerization. Our results indicate that the reaction taking place within a 20-nm electron beam gathers the material from a much larger area with

a radius of several micrometers. Surface diffusion from the surrounding area to the area under the electron beam is a thermally activated process; the probability of transfer of molecule to

neighboring adsorption state (jump) can be described by diffusion coefficient \(D={D}_{0}\exp (-{E}_{{{{{{\rm{sd}}}}}}}/{kT})\), where \({D}_{0}\) is a pre-exponential factor,

\({E}_{{{{{{\rm{sd}}}}}}}\) the activation energy of surface diffusion, \(k\) Boltzmann constant, and \(T\) temperature40; \({D}_{0}\) and \({E}_{{{{{{\rm{sd}}}}}}}\) can be obtained by

transition state theory41. For atomic species, the _E_sd is typically 5–20% of activation energy for desorption _E_des42. However, for astrochemically significant molecules on water ice,

values 20–70% of _E_des were found with no apparent relation with desorption energies1. Alongside, surface science studies indicate that values of pre-exponential factors also depart

significantly from the often-used universal value of 1 × 10−3 cm2s−1 at 300 K43. These discrepancies are associated with significant entropic contributions in the complex transition state of

organic molecules with complicated internal (vibrational and rotational) degrees of freedom43,44,45. In addition, the surface diffusion shows significant concentration dependence with

intricate cooperative effects46,47,48, highlighting the importance of studies beyond single molecule diffusion studies on monocrystalline surfaces by scanning tunneling microscopy49. Here,

we present a pilot study on the determination of the surface flow of isoprene, synthetic VOC in ultrahigh and high vacuum conditions on the ceramic surface of zirconia (tetragonal zirconia

stabilized with 3 mol.% of Y2O3) and titania (TiO2). If not stated otherwise, all substrates were fully sintered with a density over 99.9 % of the theoretical value; thus, they do not

contain a significant amount of open pores that could act as storage for organic material and interfere with the diffusion experiments. The isoprene organic adlayer was deposited by drop

casting on the surfaces thermally cleaned (600 °C, 2 h). Afterward, the sample was introduced to a vacuum environment through a load-lock chamber, where the majority of isoprene evaporated,

leaving a thin organic film on the surface. We have minimized the influence of further adsorption by performing the studies in ultrahigh vacuum (10-7 Pa) conditions. We challenge the common

thinking of contamination and present the huge opportunity we recognize in the utilization of VOC for the growth of functional nanostructures by e-beam-induced polymerization50 going beyond

the recent strategies for VOC immobilization20,32. Our study reveals that it is possible to 3D print polymeric nanostructures on rough, non-planar, non-conductive ceramic surfaces surpassing

thus the requirement of a smooth planar surface for the photoresist application required for EBL. RESULTS SUPERFLUX OF VOC ON THE CERAMIC SURFACE The sample comprising a thin layer of

isoprene on the zirconia surface was introduced to the vacuum environment of the XPS instrument through a load-lock chamber. To determine the stability and surface mobility of isoprene

molecular layers on the oxide surface, we have removed isoprene from a selected area on the zirconia surface by 2.5 keV \({{{{{{\rm{Ar}}}}}}}_{500}^{+}\) cluster beam (Fig. 1a and

Supplementary Fig. 1) and employed XPS to measure the rate of its refilling by diffusion/flow from neighboring areas by monitoring the increase of the C 1s peak intensity as a function of

time. The C 1s and Zr 3d peaks measured on the as-prepared sample before sputtering (Supplementary Fig. 2), immediately after the sputtering, and at the end of the experiment (after ~ 7.5 h)

are shown in Fig. 1b and c; the color-coded temporal evolution of these peaks is given in Fig. 1d and e. The initial isoprene layer thickness of (2.8 ± 0.5) nm was determined by calculating

the ratio of intensities of C 1s/Zr 3d photoelectron peaks in SESSA52525252 (see methods). The isoprene thickness did not significantly change during experiments, i.e., during 50 h.

\({{{{{{\rm{Ar}}}}}}}_{500}^{+}\) cluster beam efficiently removes the isoprene layer from a given area; however, the C 1s signal quickly increases in time, which is accompanied by a

decrease in Zr 3d peak as the substrate photoelectrons are attenuated in the growing isoprene layer. The intensity of C 1s peak reached after 4 h corresponds to (1.5–1.8) nm, which is about

half of the initial thickness. The time evolution of equivalent thickness for distinct sizes of sputtered areas is given in Fig. 1f. The measurement shows two regimes: up to ~0.6 nm, the

thickness rapidly increases, followed by its steady rise with a lower slope. The limiting thickness is close to the average diameter of the molecule of 0.68 nm, calculated from the molecular

mass and isoprene density in a liquid state. The growth rate also depends on the distance from the edge of the sputtered area. The further the measurement area from the edge, the slower the

rate at which the isoprene layer grows in thickness, as shown in Fig. 1g. The late steady increase of (0.0014 nm min−1) is independent of the distance from the edge. The analogous

experiments were performed with isopropanol (Supplementary Fig. 3). Here, the initial intensity increase of 0.004 nm min−1 lowered to 0.0012 nm min−1 in a steady state growth regime; both

values were independent of the sizes of the sputtered area. The initial growth rate for isopropanol was smaller than isoprene, but the steady-state rates were similar for both molecules;

these values are at the level observed for adsorption from the residual atmosphere (see below). To obtain a rough estimate of the speed of molecular flow, we have divided the distance of the

measurement area from the edge by the time necessary to form a full monolayer. For all the sputtered areas, it gives a molecular flow of (1.0 ± 0.2) μm s−1. To get a more precise estimate,

we employ a model in which we consider the diffusion of isoprene from a line source (periphery of the sputtered area). We do not consider adsorption from the residual atmosphere and

desorption of molecules to play a significant role. We have measured the adsorption within the XPS system within a period of its heavy use to get a top boundary of hydrocarbon adsorption

(see Supplementary Fig. 4). We have determined the initial effective hydrocarbon layer thickness increase to be 0.0013 nm min−1, which is below 10% of the thickness increase measured for

isoprene. Desorption of molecules during the experiment (and consequent loss of material in a given area) also cannot be ruled out. During the course of the experiment (50 h), we did not

observe a significant change in the thickness of the organic layer outside the sputtered areas. Hence, we infer that also desorption has a minor effect on the resulting isoprene thickness.

Moreover, the possible desorption goes against the adsorption lowering the impact of both contributions; hence in the following calculation, we do not include both adsorption and desorption;

the maximum error will be 10% of provided value, which is well with the confidence interval given below. By excluding adsorption and desorption, the model reduces to solving a 2D diffusion

equation with the following boundary condition: at the edge of the sputtered areas, the layer is one monolayer thick (0.68 nm) and remains constant in time. Thickness measured right after Ar

cluster sputtering was taken as the initial value in the entire sputtered area, not considering the profile of Ar beam and potential variations in sputter efficiency. The numerical solution

of the 2D diffusion equation was obtained using the finite-difference method using the Python programming language. The diffusion coefficient was estimated by comparing the measured and

calculated thickness evolution and minimizing the sum of squared errors. The resulting diffusion coefficient is (40 ± 30) μm2/s. This value lies in the range of diffusion coefficients

previously determined for systems comprising organic molecules on oxide surfaces. Computation study of _para_-hexaphenyl on \((10\bar{1}0)\) zinc oxide surface determined the value of 5 μm2

s−1 at room temperature; the fluorination of the molecule with 2 of 4F atoms decreased the diffusion coefficient value to 1 μm2 s−1 or 0.1 μm2 s−1, respectively51. In another computational

study, the diffusion coefficient decreased from 190–0.02 μm2 s−1 with increasing chain size from benzene to _para_-hexaphenyl on silica surface43. An experimental study on the diffusion of

stearic acid on the (0001) plane of the water-free surface of α-alumina gave a value52 of 20 μm2 s−1. IMMOBILIZATION OF VOC ON THE CERAMIC SURFACE Polymerization requires material and

energy. We have already determined that the surface flow of synthetic VOCs can provide enough material for localized polymerization. In this section, we will describe the immobilization of

VOCs by an e-beam to achieve high molecular weight immobile polymers. Figure 2a demonstrates the expected mechanism of 3D nanostructure formation by polymerizing the organic layer of

adsorbed VOCs transferred to the area exposed by the e-beam. Zirconia and titania were used for the substrate preparation; sintering conditions determine the density of polycrystalline

materials; for the immobilization studies, we tested substrates with up to 20% porosity with no significant impact of the porosity on the VOCs immobilization. Both smooth and rough surfaces

were prepared by fracturing or polishing the sintered materials. Two types of VOC layers were employed. The first one was the isoprene layer deposited as the liquid on the cleaned surface;

the liquid evaporated within seconds, and the prepared sample was placed into the closed box. The second kind of sample comprises a natural VOC layer from ambient conditions; according to

the previous study, the deposited layer should be similar regardless of a specific indoor environment19. The energy required for polymerization is provided locally via an electron beam. The

electrons capable of exciting and ionizing molecules have energies in the range of 5–15 eV. Electrons with energies in this range are produced as a result of the interaction of high-energy

electrons with the solid or liquid (secondary electrons)53. The interaction volume of primary electrons increases with increasing primary beam energy. To keep the interaction volume low and

polymerization localized, the primary e-beam should have low energy on the level of a few keV to penetrate only a small volume of the substrate53. We have applied the low accelerating

voltage of 0.5–5 kV, beam current 1–1000 pA, and dwell times from seconds to 72 h in SEM conditions with the aim of preparing 3D polymeric nanostructures from VOC present on the ceramic

substrate. We have tested both static and dynamic growth. In the static one, a single point was irradiated by a 10 nm beam for a given exposure dwell time (Fig. 2b). In the dynamic growth,

the desired structure was written by moving the e-beam (Fig. 2c and Supplementary Video SV1). An example of an e-beam written structure is given in Fig. 2b, d, e. The longer the e-beam

irradiation, the higher and wider the structures, as shown in Fig. 2b. The volume of written nanostructures given in Fig. 2c was calculated from the measured structure height and full width

at half maximum considering their conical shape (detailed in methods). In the case of the short-time exposure (10–200 s), the nanostructure volume linearly increases in time with the rate

(2.6 ± 0.2) × 105 nm3 s−1. The linear increase is consistent with earlier studies on electron beam growth employing focused electron beam31,33,36,38. The structure presented in Fig. 2d was

grown by the dynamic e-beam (see the attached video SV1) during 420 s; in this case, the average volume growth rate was ~7.5 × 105 nm3 s−1. Importantly, the structure also grows linearly in

height, as shown in Fig. 2c, so the material can be supplied to the top of the already-grown polymer. Considering the volume of the single isoprene molecule of 0.17 nm-3, we can estimate the

flux of monomers for the polymerization by e-beam on the level of millions of molecules per second. The nanostructures can be written in any desired shape (Fig. 2e) and also on rough plus

porous substrates (Supplementary Fig. 5). The cross-sectional TEM image of the statically written nanostructure given in Fig. 3a shows that the nanostructures have approximately a conical

shape. Their interior is not compact but comprises nanometer-size pores. The chemical composition of nanostructures was probed by TOF-SIMS (Fig. 3b, c). For this analysis, we have prepared

nanostructures with a large volume suitable for the TOF-SIMS analysis by an 18-hour-long exposition of the zirconia substrate to the e-beam radiation. As shown in Fig. 3b, the designed array

of rectangles was deformed by charging the non-conductive zirconia surface; in this way, an array of objects with increasing volume up to a few cubic micrometers built from VOC was

obtained. In addition to elements contained in the substrate (Zr, O), the mass spectra show only the presence of hydrocarbons. Figure 3c shows the hydrocarbon fragments containing up to 7C

atoms and the full spectra given in Supplementary Figs. 6 and 7 fragments up to 16C atoms within the measured range up to _m_/_z_ of 200. The measured fragments have a much larger molecular

weight than isoprene (C5H8), confirming the formation of crosslinked polymers by e-beam irradiation. Figure 3c also shows that the large hydrocarbon fragments were detected only on the

position of deposited nanostructures. DISCUSSION The isoprene layer on ceramic surfaces behaves as a fluid film with a thickness of around four molecules (2.8 ± 0.2 nm). The VOC multilayer

is also stable under ultrahigh vacuum conditions (_p_ ~ 10−6 Pa), which indicates relatively strong, liquid-like intermolecular interactions within the layer. The VOC layer is propagated on

the ceramic surface at high speed, and the high surface roughness and porosity do not present a significant obstacle (Fig. 2d). The behavior of a VOC film on a ceramic surface is similar to

liquid with zero contact angle and no gravity limitation when the thickness of the film is constant on one sample at the same conditions. Similarity with the dynamic wetting of solid by

liquid can be observed54, but further investigation is needed to define proper models. Draining material from the film leads to rapid replenishment in the depleted region, but the resulting

film thickness is reduced. The steady supply of the VOC enables the formation of polymeric nanoobjects employing e-beam immobilization. To estimate the amount of material diffusing to the

area irradiated by an e-beam, we use the mean first passage time required for diffusing particles to cross a boundary55. The mean exit time \(T\left(r\right)\) for a particle staring in a

circular area of diameter \(D\) from a concentric area with radius \(R\) by a random walk is $$T\left(r\right)=\frac{{R}^{2}-{r}^{2}}{4D},$$ where \(D\) is the diffusion coefficient. By

replacing the time average with the average per ensemble and reversing the time, we obtain the mean radius \(R\) of the circular area from which the particles reach the smaller area of

radius \(r\) as \({R}^{2}=4{DT}+{r}^{2}\). We have determined the diffusion coefficient to be ~40 μm2/s. Hence for 1 s irradiation and beam radius of 10 nm, the material for polymerization

is gathered from the area of ~500 μm2 (radius of ~12 μm). Considering a full monolayer of isoprene, the volumetric flow is over 340 × 106 nm3. s−1. The observed volume growth rate on the

spot during polymerization by e-beam is 0.26 × 106 nm3. s-1 giving 8 × 10-4 (0.08%) probability of reaction considering the same film and polymer density. This is in good agreement with our

observation that the nanostructures grew during the whole irradiation on the selected area, which shows the steady flow of reactants. A variety of ceramic surfaces can be used as

substrates—nano-sized zirconia fractured surface (Fig. 2d) or micro-sized fracture surface (Fig. 2e). We have also been successful on very rough surfaces and surfaces of titania. We expect

similar properties of VOC films on various oxides or oxide layer-covered materials but with different diffusion coefficients. The porosity of the materials is not an essential limiting

factor; a porous zirconia matrix with 20% porosity was successfully used to create nanostructures (see Supplementary Fig. 5); however, the polymerization of VOC on zirconia powder

(compressed green body) was not successful. There are several possible reasons for it: the high porosity of electrically non-conductive materials leads to surface charging and electron beam

scattering, the diffusion of organic material between the non-sintered particles is very limited, or the e-beam can also penetrate deep inside a highly porous material, causing

polymerization within the pores without us noticing it. Concerning the last point, the penetration depth of electrons into ceramic material strongly depends on the primary electron energy

(see Supplementary Table 1); at 2 keV, the penetration depth is 30–40 nm, depending on the material. Considering the relatively low density of pressed nanopowder, we can expect penetration

of electrons through particles (mean particle size is 80 nm). Furthermore, the path of the electrons is not straight (see Supplementary Fig. 8), largely increasing the interaction volume in

which the electrons can cause polymerization on pore walls. However, further investigation is necessary to quantify this phenomenon and define the organic layer flow limits on various

surfaces and the organic molecule transport within the porous media. Natural VOC can be utilized in the same way as synthetic ones. Our experiments showed that polymeric nanostructures also

grow on untreated surfaces comprising only native hydrocarbon layers. Hence, no pretreatment is necessary to fabricate nanostructures on a variety of surfaces, with the only limit being

access to the e-beam. This offers the possibility to move nanotechnology to natural material sources and on complex 3D macrostructures, create a polymeric film on inorganic surfaces, or

disarm the harmful VOCs by their immobilization. On the contrary, concentrating molecules from an organic film of unknown composition into a compact localized object makes chemical analysis

feasible. In conclusion, we have determined the molecular flow of VOC on a variety of ceramic substrates as a source of spatially localized chemical reactions. We have shown that the

isoprene multilayers are stable on the ceramic surface under ultrahigh vacuum; the molecules spread over the sample at rates of micrometers per second. The methodology presented here

provides essential quantitative insight for the modeling of surface chemical reactions and provides an answer to the question: “How far and how fast can the molecules travel on the surface

to react?” We have shown that, on average, all molecules from an area with a radius of 12 μm pass at least once under a nanometer-sized electron beam within one second. METHODS INORGANIC

SUBSTRATE Zirconia - 3 mol% yttria-stabilized tetragonal zirconia (TZ 3Yfrom Tosoh Corp., Japan) and titania powders (P25 Aeroxide, Degussa, Germany) were used as starting powders for

processing by preparation of suspensions suitable for slip casting followed by sintering, uniaxial pressing at 20 MPa followed by sintering, and direct shaping by Spark Plasma Sintering

technique. The sintering temperatures from 1100 °C to 1500 °C were used to tailor the microstructure and density of the substrates. Only fully sintered ceramic surfaces were used for

experiments reported in the main text. The porous substrates were also tested; this fact is explicitly stated at each occurrence. The selected samples were cut and polished at a level of 1

micron to achieve a flat surface or manually broken to get the fracture surface with an area of at least 20 mm2. ORGANIC LAYER DEPOSITION The organic adlayer was deposited after the thermal

cleaning of zirconia or titania surfaces. The thermal cleaning was done at a temperature of 600 °C or higher in the tubular furnace with a flow of air for at least 2 h. Subsequently, during

the cooling, the atmosphere was changed to pure nitrogen; the cleaned substrates were stored in HPLC water. The quality and reproducibility of the procedure were verified by the contact

angle measurements using the sessile-drop technique56. The contact angle of the zirconia surface decreased from 85–81° to 38–34° after the surface cleaning, indicating minor residual

contamination. After drying by the compressed air, the substrates with clean surfaces were exposed to ambient conditions or immediately covered by isoprene; such prepared samples were stored

in a closed box. The sample was introduced to a vacuum environment through a load-lock chamber, where the sample was kept for 45 min before inserting it into the main chamber with a base

pressure of 2 × 10−9 mbar. The processing steps are described in Supplementary Fig. 9. XPS ANALYSIS The X-ray photoelectron spectroscopy (XPS) analysis was performed on a Kratos Supra

spectrometer using monochromatic Al Kα X-ray radiation with 15 mA emission power. The base pressure of the instrument is 2 × 10−9 mbar; during the measurement, the pressure increased to 2 × 

10−8 mbar. The magnetic lens was used for all the measurements. Typical settings were: pass energy of 160 eV and energy step of 1 eV for survey spectra and pass energy of 20 eV and energy

step of 0.1 eV for detailed spectra. The size of the analyzed area was restricted to 110 μm in diameter by an aperture. Charge neutralization was used for all measurements. The slight

overcompensation was adjusted during the spectra processing by correcting the energy scale to the C 1s position of 285.0 eV. The isoprene layer was removed from the selected area by 2.5 keV

\({{{{{{\rm{Ar}}}}}}}_{500}^{+}\) clusters (5 eV per atom) for 1800 s. Under these conditions, we did not observe any chemical changes (reduction) in the oxide substrate. The size of the

sputtered area was determined on a reference sample comprising poly(lactic-co-glycolic) acid (PLGA) layer on a SiO2 substrate. The XPS imaging of the reference sample was carried out in the

imaging mode at the energy of Si 2p peak employing pass energy of 160 eV. Theoretical modeling of peak intensities was carried out employing the NIST Database for the Simulation of Electron

Spectra for Surface Analysis (SESSA)57, version 1.2. The model comprised a bulk oxide layer (ZrO2) covered with a uniform hydrocarbon layer with an atomic density of 7.8 × 1022 cm−3

determined from isoprene molecular mass and density in the liquid state. SIMS, SEM, AND AFM ANALYSIS Secondary Ion Mass Spectrometry (IONTOF TOF-SIMS5) was employed for elemental analysis of

e-beam fabricated nanostructures. We used the instrument in the imaging mode that provides enhanced lateral resolution of ~0.8 µm and sufficient mass resolution of ~140 at C5 peak. Bi+

primary ions with the following parameters were used: impact energy of 30 keV, impact angle of 45°, pulsed primary current of ~3 pA, and raster size 25 µm × 25 µm. Cs+ co-sputtering was

performed in the non-interlaced regime with a crater size of 120 µm × 120 µm, an impact angle of 45°, and an energy of 500 eV. The base pressure in the analytical chamber was ~5 × 10−10

mbar. SEM and AFM analysis was performed by two separate SEM instruments—Tescan Lyra3 and FEG-SEM Carl Zeiss ULTRAPLUS. The typical procedure conducted by the LYRA3 SEM was that the chamber

was cleaned with a plasma decontaminator at a pressure of 50 Pa for 10 min, and the shape and dwell time (electron dose) were controlled by DrawBeam2 software. The parameters for

nanostructure formation were the following: accelerating voltage of 0.5–5 kV, current from 1–1000 pA, and dwell time from seconds to 72 h. The grown structures were analyzed by AFM

(Nenovision Litescope) directly inside the SEM chamber. We did not find any significant changes in the shape of the polymer structures that were measured at ambient temperature after two

weeks. Akiyama Probe was used for AFM imaging with the specification: cantilever length 310 μm, thickness 3,7 μm, width 30 μm, n-type, highly doped silicon; Tip radius < 15 nm, tip height

28 μm; Constant force 5 N/m; Resonance frequency 40–60 kHz. Dimensions and shapes of structures were analyzed in Gwyddion v2.4758. DATA AVAILABILITY The data that support the findings of

this study are available in Figshare with the identifier https://doi.org/10.6084/m9.figshare.2412519659. REFERENCES * Furuya, K. et al. Diffusion activation energy and desorption activation

energy for astrochemically relevant species on water ice show no clear relation. _Astrophys. J. Lett._ https://doi.org/10.3847/2041-8213/ac78e9 (2022). * Murzin, D. Y. Kinetics of

heterogeneous single‐site catalysis. _ChemCatChem_ 15, https://doi.org/10.1002/cctc.202201082 (2022). * Xiong, M., Gao, Z. & Qin, Y. Spillover in heterogeneous catalysis: new insights

and opportunities. _ACS Catal._ 11, 3159–3172 (2021). CAS  Google Scholar  * Conner, W. C. & Falconer, J. L. Spillover in heterogeneous catalysis. _Chem. Rev._ 95, 759–788 (1995). CAS 

Google Scholar  * Braun, S., Salaneck, W. R. & Fahlman, M. Energy-level alignment at organic/metal and organic/organic interfaces. _Adv. Mater._ 21, 1450–1472 (2009). CAS  Google Scholar

  * Turetta, N., Sedona, F., Liscio, A., Sambi, M. & Samorì, P. Au(111) surface contamination in ambient conditions: unravelling the dynamics of the work function in air. _Adv. Mater.

Interfaces_ https://doi.org/10.1002/admi.202100068 (2021). * Evans, S. Correction for the effects of adventitious carbon overlayers in quantitative XPS analysis. _Surf. Interface Anal._ 25,

924–930 (1997). CAS  Google Scholar  * Mangolini, F., McClimon, J. B., Rose, F. & Carpick, R. W. Accounting for nanometer-thick adventitious carbon contamination in X-ray absorption

spectra of carbon-based materials. _Anal. Chem._ 86, 12258–12265 (2014). CAS  PubMed  Google Scholar  * Den, W., Hu, S.-C., Garza, C. M. & Ali Zargar, O. Review—Airborne molecular

contamination: recent developments in the understanding and minimization for advanced semiconductor device manufacturing. _ECS J. Solid State Sci. Technol._

https://doi.org/10.1149/2162-8777/aba080 (2020). * Morrison, G. Recent advances in indoor chemistry. _Curr. Sustain./Renew. Energy Rep._ 2, 33–40 (2015). Google Scholar  * Ault, A. P. et al.

Indoor surface chemistry: developing a molecular picture of reactions on indoor interfaces. _Chem_. 6, 3203–3218 (2020). CAS  PubMed  PubMed Central  Google Scholar  * Farmer, D. K.

Analytical challenges and opportunities for indoor air chemistry field studies. _Anal. Chem._ 91, 3761–3767 (2019). CAS  PubMed  Google Scholar  * Brown, S. K., Sim, M. R., Abramson, M. J.

& Gray, C. N. Concentrations of Volatile organic-compounds in indoor air - a review. _Indoor Air-Int. J. Indoor Air Qual. Clim._ 4, 123–134 (1994). CAS  Google Scholar  * Zimmerling, T.

& Batlogg, B. Improving charge injection in high-mobility rubrene crystals: from contact-limited to channel-dominated transistors. _J. Appl. Phys._ 115, 164511 (2014). Google Scholar  *

Meyer, J., Shu, A., Kröger, M. & Kahn, A. Effect of contamination on the electronic structure and hole-injection properties of MoO3/organic semiconductor interfaces. _Appl. Phys. Lett._

96, 133308 (2010). Google Scholar  * Phark, J. H., Duarte, S. Jr., Kahn, H., Blatz, M. B. & Sadan, A. Influence of contamination and cleaning on bond strength to modified zirconia.

_Dent. Mater._ 25, 1541–1550 (2009). CAS  PubMed  Google Scholar  * Williams, D. F., Kellar, E. J. C., Jesson, D. A. & Watts, J. F. Surface analysis of 316 stainless steel treated with

cold atmospheric plasma. _Appl. Surf. Sci._ 403, 240–247 (2017). CAS  Google Scholar  * Wu, C. C., Wei, C. K., Ho, C. C. & Ding, S. J. Enhanced hydrophilicity and biocompatibility of

dental zirconia ceramics by oxygen plasma treatment. _Materials_ 8, 684–699 (2015). CAS  PubMed  PubMed Central  Google Scholar  * Landoulsi, J. et al. Organic adlayer on inorganic

materials: XPS analysis selectivity to cope with adventitious contamination. _Appl. Surf. Sci._ 383, 71–83 (2016). CAS  Google Scholar  * Li, X. et al. Adsorption materials for volatile

organic compounds (VOCs) and the key factors for VOCs adsorption process: a review. _Sep. Purif. Technol._ https://doi.org/10.1016/j.seppur.2019.116213 (2020). * Hwang, S. Y. et al. Removal

and recycling of volatile organic compounds (VOCs) adsorbed on activated carbons using in situ vacuum systems. _Int. J. Environ. Sci. Technol._ 16, 7827–7836 (2019). CAS  Google Scholar  *

Vladar, A. & Postek, M. Electron Beam-Induced Sample Contamination in the SEM. _Microsc. Microanal._ https://doi.org/10.1017/s1431927605507785 (2005). * Allgair, J. A., Vladár, A. E.,

Raymond, C. J., Purushotham, K. P. & Postek, M. T. in _Metrology, Inspection, and Process Control for Microlithography XXII_ (2008). * Chen, Y. F. Nanofabrication by electron beam

lithography and its applications: a review. _Microelectron. Eng._ 135, 57–72 (2015). CAS  Google Scholar  * Huth, M., Porrati, F. & Dobrovolskiy, O. V. Focused electron beam induced

deposition meets materials science. _Microelectron. Eng._ 185-186, 9–28 (2018). CAS  Google Scholar  * Utke, I., Hoffmann, P. & Melngailis, J. Gas-assisted focused electron beam and ion

beam processing and fabrication. _J. Vac. Sci. Technol. B_ https://doi.org/10.1116/1.2955728 (2008). * Neumann, C., Wilhelm, R. A., Küllmer, M. & Turchanin, A. Low-energy electron

irradiation induced synthesis of molecular nanosheets: influence of the electron beam energy. _Faraday Discuss._ 227, 61–79 (2021). CAS  PubMed  Google Scholar  * Cechal, J. & Sikola, T.

Flexible foils formed by a prolonged electron beam irradiation in scanning electron microscope. _Appl. Surf. Sci._ 423, 538–541 (2017). CAS  Google Scholar  * Rykaczewski, K., Marshall, A.,

White, W. B. & Fedorov, A. G. Dynamic growth of carbon nanopillars and microrings in electron beam induced dissociation of residual hydrocarbons. _Ultramicroscopy_ 108, 989–992 (2008).

CAS  PubMed  Google Scholar  * Hettler, S. et al. Carbon contamination in scanning transmission electron microscopy and its impact on phase-plate applications. _Micron_ 96, 38–47 (2017). CAS

  PubMed  Google Scholar  * Lau, D., Hughes, A. E., Muster, T. H., Davis, T. J. & Glenn, A. M. Electron-beam-induced carbon contamination on silicon: characterization using raman

spectroscopy and atomic force microscopy. _Microsc. Microanal._ 16, 13–20 (2010). CAS  PubMed  Google Scholar  * Liu, Y. et al. Challenges and opportunities in molecular-level indoor surface

chemistry and physics. _Cell Rep. Phys. Sci._ 1, 100256 (2020). Google Scholar  * Müller, K.-H. Elektronen-Mikroschreiber mit geschwindigkeitsgesteuerter Strahlführung. _Optik_ 33, 296–311

(1971). Google Scholar  * Pepponi, G. et al. Analysis of organic contaminants on Si wafers with TXRF-NEXAFS. _Spectrochim. Acta B_ 58, 2245–2253 (2003). Google Scholar  * Meyer, J. C.,

Girit, C. O., Crommie, M. F. & Zettl, A. Hydrocarbon lithography on graphene membranes. _Appl. Phys. Lett._ https://doi.org/10.1063/1.2901147 (2008). * Miura, N., Ishii, H., Shirakashi,

J., Yamada, A. & Konagai, M. Electron-beam-induced deposition of carbonaceous microstructures using scanning electron microscopy. _Appl. Surf. Sci._ 113, 269–273 (1997). Google Scholar 

* Amman, M. et al. Atomic force microscopy study of electron beam written contamination structures. _J. Vac. Sci. Technol. B_ 14, 54–62 (1996). CAS  Google Scholar  * Kislov, N. A. Direct

stem fabrication and characterization of self-supporting carbon structures for nanoelectronics. _Scanning_ 15, 212–218 (1993). Google Scholar  * Guenther, A. et al. A global-model of natural

volatile organic-compound emissions. _J. Geophys. Res.-Atmospheres_ 100, 8873–8892 (1995). CAS  Google Scholar  * Seebauer, E. G. & Allen, C. E. Estimating Surface-Diffusion

Coefficients. _Prog. Surf. Sci._ 49, 265–330 (1995). CAS  Google Scholar  * Ibach, H. _Physics of Surfaces and Interfaces_. 1 edn, (Springer Berlin, Heidelberg, 2006). * Oura, K., Katayama,

M., Zotov, A. V., Lifshits, V. G. & Saranin, A. A. _Surface Science_. 1 edn, 440 (Springer Berlin, Heidelber, 2013). * Miletic, M., Palczynski, K. & Dzubiella, J. Quantifying

entropic barriers in single-molecule surface diffusion. _J. Chem. Phys._ 153, 164713 (2020). CAS  PubMed  Google Scholar  * Hedgeland, H. et al. Mass transport in surface diffusion of van

der Waals bonded systems: boosted by rotations. _J. Phys. Chem. Lett._ 7, 4819–4824 (2016). CAS  PubMed  Google Scholar  * Gehrig, J. C. et al. Surface single-molecule dynamics controlled by

entropy at low temperatures. _Nat. Commun._ 8, 14404 (2017). CAS  PubMed  PubMed Central  Google Scholar  * Naumovets, A. G. Collective surface diffusion: an experimentalist’s view. _Phys.

A._ 357, 189–215 (2005). Google Scholar  * Valiullin, R., Kortunov, P., Kärger, J. & Timoshenko, V. Surface self-diffusion of organic molecules adsorbed in porous silicon. _J. Phys.

Chem. B_ 109, 5746–5752 (2005). CAS  PubMed  Google Scholar  * Bertram, C., Fang, W., Pedevilla, P., Michaelides, A. & Morgenstern, K. Anomalously low barrier for water dimer diffusion

on Cu(111). _Nano Lett_. 19, 3049–3056 (2019). * Antczak, G., Kamiński, W., Sabik, A., Zaum, C. & Morgenstern, K. Complex surface diffusion mechanisms of cobalt phthalocyanine molecules

on Ag(100). _J. Am. Chem. Soc_. 137, 14920–14929 (2015). * Acikgoz, C., Hempenius, M. A., Huskens, J. & Vancso, G. J. Polymers in conventional and alternative lithography for the

fabrication of nanostructures. _Eur. Polym. J._ 47, 2033–2052 (2011). CAS  Google Scholar  * Miletic, M. et al. Impact of polarity on anisotropic diffusion of conjugated organic molecules on

the (101̅0) zinc oxide surface. _J. Phys. Chem. C_ 123, 6549–6559 (2019). CAS  Google Scholar  * Yang, R. T., Fenn, J. B. & Haller, G. L. Surface diffusion of stearic acid on aluminum

oxide. _AIChE J._ 20, 735–742 (1974). CAS  Google Scholar  * Drobny, J. G. _Radiation tEchnology for Polymers_. 3rd edn, 338 (CRC Press, 2021). * de Gennes, P. G. in _Fundamentals of

Adhesion_ (ed Lee, L. -H.) 173–179 (Springer US, 1991). * Simpson, M. J., VandenHeuvel, D. J., Wilson, J. M., McCue, S. W. & Carr, E. J. Mean exit time for diffusion on irregular

domains. _New J. Phys._ https://doi.org/10.1088/1367-2630/abe60d (2021). * Birch, W., Carré, A. & Mittal, K. L. in _Developments in_ Sur_face Contamination and Cleaning_ (eds Rajiv Kohli

& Mittal, K. L.) 693–723 (William Andrew Publishing, 2008). * Smekal, W., Werner, W. S. M. & Powell, C. J. Simulation of electron spectra for surface analysis (SESSA): a novel

software tool for quantitative Auger-electron spectroscopy and X-ray photoelectron spectroscopy. _Surf. Interface Anal._ 37, 1059–1067 (2005). CAS  Google Scholar  * Necas, D. &

Klapetek, P. Gwyddion: an open-source software for SPM data analysis. _Cent. Eur. J. Phys._ 10, 181–188 (2012). Google Scholar  * Salamon, D., Bukvišová, K., Jan, V., Potoček, M. &

Čechal, J. Superflux of an organic adlayer towards its local reactive immobilization: Primary Data. https://doi.org/10.6084/m9.figshare.24125196.v1 (2023). Download references

ACKNOWLEDGEMENTS CzechNanoLab project LM2018110 funded by MEYS CR is gratefully acknowledged for the financial support of the measurements at CEITEC Nano Research Infrastructure. We thank

Jan Čupera for assistance with the SEM. AUTHOR INFORMATION AUTHORS AND AFFILIATIONS * CEITEC - Central European Institute of Technology, Brno University of Technology, Purkyňova 123, 612 00,

Brno, Czech Republic David Salamon, Kristýna Bukvišová, Michal Potoček & Jan Čechal * Fakulty of Mechanical Engineering, Brno University of Technology, Technická 2896/2, 616 69, Brno,

Czech Republic Vít Jan & Jan Čechal Authors * David Salamon View author publications You can also search for this author inPubMed Google Scholar * Kristýna Bukvišová View author

publications You can also search for this author inPubMed Google Scholar * Vít Jan View author publications You can also search for this author inPubMed Google Scholar * Michal Potoček View

author publications You can also search for this author inPubMed Google Scholar * Jan Čechal View author publications You can also search for this author inPubMed Google Scholar

CONTRIBUTIONS D.S. initiated, conceptualized, and supervised the research. D.S., K.B., and V.J. performed the electron beam growth studies and analyzed the data, D.S. interpreted the data.

M.P. performed the SIMS measurements and analyzed data. K.B. developed the code and solved the diffusion equation. J.Č. developed the XPS methodology, performed the experiments, analyzed,

and interpreted the data. D.S. and J.Č. wrote the manuscript. All authors discussed the results and contributed to the final manuscript. CORRESPONDING AUTHORS Correspondence to David Salamon

or Jan Čechal. ETHICS DECLARATIONS COMPETING INTERESTS The authors declare no competing interests. PEER REVIEW PEER REVIEW INFORMATION _Communications Chemistry_ thanks Patrik Hoffmann and

the other anonymous, reviewers for their contribution to the peer review of this work. ADDITIONAL INFORMATION PUBLISHER’S NOTE Springer Nature remains neutral with regard to jurisdictional

claims in published maps and institutional affiliations. SUPPLEMENTARY INFORMATION SUPPLEMENTARY INFORMATION DESCRIPTION OF ADDITIONAL SUPPLEMENTARY FILES SUPPLEMENTARY VIDEO 1 RIGHTS AND

PERMISSIONS OPEN ACCESS This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any

medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The

images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not

included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly

from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. Reprints and permissions ABOUT THIS ARTICLE CITE THIS ARTICLE Salamon, D.,

Bukvišová, K., Jan, V. _et al._ Superflux of an organic adlayer towards its local reactive immobilization. _Commun Chem_ 6, 225 (2023). https://doi.org/10.1038/s42004-023-01020-2 Download

citation * Received: 26 April 2023 * Accepted: 02 October 2023 * Published: 18 October 2023 * DOI: https://doi.org/10.1038/s42004-023-01020-2 SHARE THIS ARTICLE Anyone you share the

following link with will be able to read this content: Get shareable link Sorry, a shareable link is not currently available for this article. Copy to clipboard Provided by the Springer

Nature SharedIt content-sharing initiative